Magnesia Stabilized Zirconia Rods stand out for their exceptional resistance to thermal shock and erosion, alongside their minimal thermal expansion and outstanding non-wetting qualities. These rods, made from Zirconia (ZrO2), are recognized for their refractory and insulating capabilities. Capable of achieving a clean melt at temperatures above 1900°C, they are specifically designed for the melting of superalloys and precious metals. Additionally, they exhibit remarkable chemical inertness, unparalleled resistance to thermal shock up to 2200°C, and robust corrosion resistance against both acids and alkalis.
Composition |
Content % |
ZrO2 |
95.3 |
MgO |
2.2 |
CaO |
0.2 |
Al2O3 |
0.7 |
TiO2 |
0.2 |
Fe2O3 |
0.2 |
SiO2 |
1.2 |
Physical Properties |
|
Density |
4.5g/cc |
Porosity |
18% |
MOR @R.T. |
3500psi |
Magnesia Stabilized Zirconia Rods are versatile in application, suitable for use in shafts, plungers, seals, the automotive sector, oil exploration machinery, and as insulation in electrical devices. Their high density, bending strength, and fracture toughness also make them ideal for producing ceramic knives and replacement parts for ceramic hair clippers.
Magnesia Stabilized Zirconia Rods are carefully packaged to ensure their integrity and quality during transport and storage. The rods are typically secured in protective wrapping or padding to prevent any damage or contamination. They may be placed in sturdy, custom-designed boxes or crates that are suitable for the rods' dimensions and weight, ensuring they remain undamaged throughout handling, shipping, and delivery. The packaging process is meticulously managed to meet the highest standards of safety and environmental considerations, facilitating safe arrival at their destination ready for industrial or commercial use.